In vivo osseointegration and erosion of nacre screws in an animal model.

The use of resorbable devices for osteosynthesis has become a subject of interest. Nacre has been proposed as a resorbable and osteoconductive material favoring bone apposition without triggering an inflammatory reaction. We compared the in vivo osseointegration and erosion of nacre screws in an animal model with titanium screws. Implantation of similar nacre and titanium screws was performed in the femoral condyles of adult rats. Animals (n = 41) were randomized in four groups sacrificed at day one, 1, 6, and 12 months. Microcomputed tomography (microCT) allowed 3D morphometry of erosion of nacre. Osseointegration was measured as the volume of trabecular bone bone volume/tissue volume (BV/TV) in a standardized volume of interest around each screw. Undecalcified bone histology was also done. Gross examination revealed a similar clinical osseointegration for titanium and nacre screws. A progressive erosion of nacre screws, but no erosion of titanium screws, was observed in microCT. The volume of nacre screws progressively decreased over time whereas no modification occurred for titanium. For titanium screws, BV/TV remained stable throughout the study. For nacre screws, the BV/TV decrease was not statistically different. A significant difference was found between nacre and titanium screws at 6 months but not at 12 months. The screw heads, outside the bone shaft, were not eroded even after 12 months. Erosion of nacre occurred during the entire study period, only within the bone shaft in direct contact with bone marrow. Bone apposition was observed on nacre surfaces without signs of erosion. Nacre is a promising biomaterial in maxillofacial surgery.

Giant cells and osteoclasts present in bone grafted with nacre differ by nuclear cytometry evaluated by texture analysis.

Nacre (mother of pearl) is a natural biomaterial used to prepare orthopedic devices. We have implanted screws and plates made with nacre in five sheeps. Bone were harvested after two months and embedded in poly(methyl methacrylate). Blocks were saws and the thick slabs were grinded, polished and surface stained. Sections were photographed at an ×1000 magnification. Giant cells were found in contact with nacre in eroded areas and true osteoclasts were found at distance in the neighboring bone in Howship lacunae. A texture analysis of the nuclei of giant cells and osteoclasts was done using the run-length method of the MaZda freeware. The size of the nuclei was reduced in osteoclast and their mean gray level appeared reduced. Texture analysis revealed that chromatin had a completely different pattern in giant cells when compared to osteoclasts. Giant cells had a fine repartition of the chromatin with large clear areas around prominent nucleoli. On the contrary, osteoclast nuclei had chromatin blocks evenly dispersed in the nuclei. This reflects the different origin of these cells expressing different functions.